Note: Print settings for this material may not be available yet on Form 3L and Form 3BL printers. Please visit our support page for more information.
Additional resin compatibility information is available on our site
Why Choose BioMed Clear Resin?
Fuel medical innovation using 3D printing and BioMed Clear Resin for producing end-use devices where performance and biocompatibility are critical.
- Medical-Grade Material
Leverage a material manufactured within our Quality Management Systems, with strict adherence to ISO 13485.
- Transparent
Visibility through parts allows light to pass through.
- Biocompatible and Sterilizable Parts
Testing conducted by Formlabs for common use cases is intended to instill confidence that this material is suitable for biocompatible applications.
- Excellent Definition
Produce parts and assemblies with complex designs and geometries.
Applications
Use BioMed Clear Resin for producing rigid, transparent parts for point-of-care and medical manufacturing applications requiring biocompatibility.
Consider BioMed Clear Resin for:
End-use devices
Models for visualization and implant sizing
Biocompatible prototypes, molds, jigs + fixtures
Gas pathway connectors, adapters + devices
Post-cured at 60ºC for 60 min
1* Material properties may vary based on part geometry, print orientation, print settings, temperature, and disinfection or sterilization methods used.
2* Data were measured on post-cured samples printed on a Form 3B printer with 100 µm BioMed Clear Resin settings, washed in a Form Wash for 20 minutes in 99% Isopropyl Alcohol, and post-cured at 60°C for 60 minutes in a Form Cure.
3* BioMed Clear Resin was tested at NAMSA World Headquarters, OH, USA.
Download BioMed Clear Resin Technical Data Sheet See resin compatibilityPost-Processing
Form Wash Settings
DURATION
15 min + 5 min or until clean
NOTES
Wash until clean in ≥ 99% IPA. Biocompatible resins must be washed in a dedicated biocompatible IPA bath. They cannot be washed in IPA that is cross-contaminated with other resins.
Form Cure Settings
DURATION
60 min
TEMPERATURE
60 °C
NOTES
Follow the post-curing indications to achieve maximum material properties.