Bambu Lab High Temperature Plate Spare Sheet
- Home
- Shop
- Parts & Accessories, Bambu Lab-Accessories
- Bambu Lab High Temperature Plate Spare Sheet
Bambu Lab High Temperature Plate Spare Sheet
“Bambu Lab’s High-Temperature Plate Spare Sheet is tailored for the X1 & P1P series. Offering uniform heat distribution for impeccable 3D printing results.”
- Description
Description
Bambu Lab
Spare Sheet for Bambu High Temperature Plate
Overview
The Bambu High-Temperature Sheet (Smooth PEI) is a sheet with an adhesive side. For replacing the sheet on your High-Temperature Plate.
Compatibility
X1 Series and P1 Series
Note
The Bambu High-Temperature sheet is easy to replace and install.
- After tearing off the original sheet, please use alcohol to wipe the surface clean. Make sure the surface stays dry while applying a new sheet.
- You can use an anhydrous ethanol solution or isopropanol solution with a concentration of over 90% to wipe the plate.
- You can also use detergent and water to clean the surface.
It is also best to use special solid glue (Glue Stick for Build Plate) before printing to avoid damage during model removal.
HINTS: The STL file of the “Fixture” shown in the video can be found in the printer internal memory or download from here. https://wiki.bambulab.com/en/knowledge-sharing/Links-to-STL-models
How to print your Film Sticking Fixture?
Bambu Lab 3D printer with two film sticking fixture models to help you change spare sheets. Print ‘Film Sticking Fixture’ from the built-in files!
Recommended settings for Bambu High-Temperature Plate
Please note that other slicer settings might need to be adjusted based on the printed model and the filament requirements.
Hotbed Temperature | Glue Stick Required? | Upper Glass Cover Plate Removed? |
PLA/PLA-CF/PLA-GF | 45~60℃ | Recommended | Yes |
ABS | 90~100℃ | Recommended | No |
PETG | 80℃ | Yes | Yes |
TPU | 35℃ | Recommended | Yes |
ASA | 90~100℃ | Recommended | No |
PVA | 45~60℃ | Recommended | Yes |
PC/PC-CF | 100~110℃ | Yes | No |
PA/PAHT-CF | 100~110℃ | Yes | No |