3D print strong, precise concept models and prototypes that bring your ideas to life with Formlabs’ library of Standard Resins. With a matte surface finish, opaque appearance, and precise details, prints are ready to use right off the printer. Their neutral undertone makes a great base for parts that will eventually be painted or undergo other finishing processes.
Why Choose White Resin 5L?
Leverage White Resin 5L to iterate on high-resolution prototypes and models that capture astonishing detail without sacrificing strength.
- Opaque and Matte
Produce prints with smooth, opaque surfaces ideal for model making, painting, and looks-like prototyping. - High Part Quality
Show off fine details and iterate on designs when you want to focus on form alone. - Ease of Use
Start using your parts quickly, as Formlabs’ Standard Resins only need minimal post-processing. - Neutral Undertone
Paint or use other finishing processes to elevate your model or prototype.
Applications
White Resin supports high detail with a smooth, matte surface finish with great mechanical properties.
Consider White Resin 5L for:
- General purpose prototyping and design
- Models with very small features and intricate details
- Base for painted prints
- Presentation-ready pieces
Download White Resin Technical Data Sheet
* Material properties may vary based on part geometry, print orientation, print settings, and temperature. Data was obtained from parts printed using Form 2, 100 μm, Clear settings and post-cured with 1.25 mW/cm³ of 405 nm LED light for 60 minutes at 60°C.
Post-Processing
Form Wash Settings
DURATION
10 min in IPA
NOTES
When using a single wash bucket, residue from previously washed parts deposits on part surfaces.
If washing darker-colored materials like Black Resin in the same wash bucket as lighter-colored materials like White Resin or Clear Resin, some color transfer may occur.
Form Cure Settings
DURATION
30 min
TEMPERATURE
60 °C
NOTES
All standard opaque Formlabs resins (including Grey, Black, White, Color, and Model Resin) have equivalent mechanical properties.
While the recommended post-cure time is 30 minutes, post-curing for 60 minutes will result in a small additional gain in tensile modulus. This post-cure setting can be used with any of these resins.